| 物 性 |
条件 |
単位 |
テスト方法
|
GP-22 |
| ISO |
ASTM |
| Mechanical |
| 引っ張り強度(降伏点） |
- |
kg/cm2 |
527-2 |
D638 |
470 |
| 引っ張り強度(破断点) |
- |
kg/cm2 |
527-2 |
D638 |
430 |
| 伸び率(降伏点) |
- |
% |
527-2 |
D638 |
2.7 |
| 伸び率(破断点) |
- |
% |
527-2 |
D638 |
20 |
| 引っ張り弾性率 |
- |
kg/cm2 |
527-2 |
D638 |
23500 |
| 曲げ強度 |
- |
kg/cm2 |
178 |
D790 |
700 |
| 曲げ弾性率 |
- |
kg/cm2 |
178 |
D790 |
24000 |
| Ｒｏｃｋｗｅｌｌ硬度 |
- |
R-scale |
- |
D785 |
103 |
| Impact |
| 衝撃強度
(Charpy) |
23℃ |
KJ/m2 |
179/1eU |
- |
210 |
| -30℃
|
KJ/m2 |
179/1eU |
- |
110 |
| 衝撃強度 (Charpy
notched) |
23℃ |
KJ/m2 |
179/1eA |
- |
23 |
| -30℃
|
KJ/m2 |
179/1eA |
- |
8 |
| 衝撃強度 (Izod)
|
23℃
|
KJ/m2 |
180/1U |
- |
150-n.b. |
| -30℃
|
KJ/m2 |
180/1U |
- |
90 |
| 衝撃強度 (Izod
notched) |
23℃ |
KJ/m2 |
180/1A |
- |
25 |
| -30℃ |
KJ/m2 |
180/1A |
- |
8 |
| 衝撃強度 (Izod
notched, 3.2mm) |
23℃
|
J/m
|
- |
D256 |
250 |
| -30℃
|
J/m
|
- |
D256 |
100 |
| Thermal |
| Ｖｉｃａｔ軟化点(VST, B/50)
|
5Kg load |
℃ |
306 |
- |
97 |
| 熱変形温度
(HDT, annealed) |
A-18.6Kg load |
℃ |
- |
D648 |
99 |
| B-
4.6Kg load |
℃ |
- |
D648 |
103 |
| 連続使用可能な温度 |
Molded parts |
℃ |
- |
- |
80 |
| 線膨張係数 |
- |
(1/K)×10-5 |
DIN53752 |
- |
8-11 |
| 熱伝導度 (-40℃~80℃)
|
- |
W/(K.m) |
DIN52612 |
- |
0.17 |
| Physical |
密 度
|
- |
g/cm3 |
1183 |
D792 |
1.04 |
| 流動性指数 |
200℃/5Kg |
cm3/10min |
1133 |
D1238 |
1.6 |
| |
220℃/10Kg |
cm3/10min |
1133 |
D1238 |
20 |
| 成型収縮率(120×15×10mm)
|
- |
% |
DIN16901 |
D955 |
0.3-0.6 |
| 吸湿率 |
- |
% |
DIN53495-1L |
D570 |
0.3 |
| 難燃性 |
- |
Class |
UL 94 |
HB |
|
 |
 |
|
 |
| |
|
|
| TYPICAL PROPERTIES1 |
TYPICAL VALUE |
UNIT |
STANDARD |
| MECHANICAL |
| Tensile Str, yld, Type I, 50
mm/min |
67 |
MPa |
ASTM D 638 |
| Tensile Elong, brk Type I, 50
mm/min |
50 |
% |
ASTM D 638 |
| Flex Stress, yld, 2.6 mm/min,
100 mm span |
103 |
Mpa |
ASTM D 790 |
| Flex Mod, 2.6 mm/min, 100 mm
span |
2690 |
Mpa |
ASTM D 790 |
| IMPACT |
| Izod Impact notched, 23℃ |
534 |
J/m |
ASTM D 256 |
| Instrumented Impact Energy @
peak, 23℃ |
61 |
J |
ASTM D 3763 |
| Instrumented Impact Energy @
peak, -30℃ |
54 |
J |
ASTM D 3763 |
| THERMAL |
| HDT, 1.84 Mpa, 3.2 mm, unannealed |
88 |
℃ |
ASTM D 648 |
| HDT, 1.82 Mpa, 6.4 mm, unannealed |
91 |
℃ |
ASTM D 648 |
| Relative Temp Index, Elec |
85 |
℃ |
UL 746B |
| Relative Temp Index, w/impact |
85 |
℃ |
UL 746B |
| Relative Temp Index, Mech w/o
impact |
85 |
℃ |
UL 746B |
| PHYSICAL |
| Specific Gravity |
1.18 |
- |
ASTM D 792 |
| Mold Shrinkage flow, 3.2 mm |
0.4-0.6 |
% |
ASTM D 955 |
| Mold Shrinkage, xflow, 3.2 mm |
0.4-0.6 |
% |
ASTM D 955 |
| Melt Flow Rate, 260℃/2.16kgf |
14.5 |
g/10 min |
ASTM D 1238 |
| Spiral Flow, 260℃,10 ips, 3.175
X 1524 mm |
685.8 |
mm |
- |
| ELECTRIAL |
| Arc Resistance, Tungsten {PLC} |
6 |
PLC Code |
ASTM D 495 |
| Hot Wire Ignition {PLC} |
2 |
PLC Code |
UL 746A |
| High Voltage Arc Track Rate
{PLC} |
3 |
PLC Code |
UL 746A |
| High Ampere
Arc Ign, surface {PLC} |
0 |
PLC Code |
UL 746A |
| Comparative Tracking Index (UL)
{PLC} |
2 |
PLC Code |
UL 746A |
| Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
| Surface Resistivity, ROA |
>1.E+15 |
cm |
IEC 60093 |
| Dielectric Strength, in oil,
0.8 mm |
35 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil,
1.6 mm |
25 |
kV/mm |
IEC 60243-1 |
| Dielectric Strength, in oil,
3.2 mm |
17 |
kV/mm |
IEC 60243-1 |
| TYPICAL PROPERTIES1 |
TYPICAL VALUE |
UNIT |
STANDARD |
| Relative Permittivity, 50/60
Hz |
2.8 |
- |
IEC 60250 |
| Relative Permittivity,
1 MHz |
2.7 |
- |
IEC 60250 |
| Dissipation Factor, 50/60 Hz |
0.004 |
- |
IEC 60250 |
| Dissipation Factor, 1 MHz |
0.008 |
- |
IEC 60250 |
| Flame Characteristics |
|
|
|
| UL Recognized, 94HB Flame Class
Rating (3) |
0.7 |
mm |
UL 94 |
| UL Recognized, 94V-1 Flame Class
Rating (3) |
1.2 |
mm |
UL 94 |
| UL Recognized, 94V-0 Flame Class
Rating (3) |
1.5 |
mm |
UL 94 |
| UL Recognized, 94-5VA Rating
(3) |
3.4 |
mm |
UL 94 |
| UL Recognized, 94-5VB Rating
(3) |
2 |
mm |
UL 94 |
| CSA (see File for Complete listing) |
LS88480 |
File No. |
CSA LISTED |
| PROCESSNG
PARAMETERS |
TYPICAL VALUE |
UNIT |
| Injection
Molding |
|
|
| Drying
Temperature |
80-90 |
℃ |
| Drying
Time |
3-4 |
hrs |
| Drying
Time (Cumulative) |
0.04 |
% |
| Melt
Temperature |
245-275 |
℃ |
| Nozzle
Temperature |
245-275 |
℃ |
| Front-Zone
3 Temperature |
245-275 |
℃ |
| Middle-Zone
2 Temperature |
220-265 |
℃ |
| Rear-Zone1
Temperature |
220-255 |
℃ |
| Mold
Temperature |
60-80 |
℃ |
| Back
Pressure |
0.3-0.7 |
Mpa |
| Screw
Speed |
40-70 |
rpm |
| Shot
to Cylinder Size |
30-80 |
% |
| Vent
Depth |
0.038-0.076 |
mm |
|
|
 |
 |
 |
 |
 |
| |
|
|
| Properties2 |
TestMethod |
English |
SI |
| Value |
Units |
Value |
Units |
| Physical |
| Melt Flow rate
(300℃/1.2kg) |
ASTM D1238 |
22 |
g/10 min |
22 |
g/10 min |
| Density |
ASTM D792 |
1.20 |
|
1,200 |
Kg/m3 |
| Mould Shrinkage |
ASTM D955 |
0.005~0.007 |
in/in |
0.005~0.007 |
mm/mm |
| Water Absorption
@ 24hrs, 23℃ |
ASTM D570 |
0.15 |
% |
0.15 |
% |
| @ equilibrium,
50%RH, 23℃ |
ASTM D570 |
0.32 |
% |
0.32 |
% |
| Optical |
| Refractive index.
nD |
ASTM D542 |
1.586 |
|
1.586 |
|
| Light Transmittance |
ASTM D1003 |
89 |
% |
89 |
% |
| Haze |
ASTM D1003 |
0.7~1.5 |
% |
0.7~1.5 |
% |
| Thermal |
| Deflection Temperature
Under Load(DTUL)@ 4mm |
ASTM D648 |
|
|
|
|
| @66 psi (0.45Mpa),
anneled |
|
288 |
? |
142 |
℃ |
| @264 psi (1.8Mpa),
anneled |
|
282 |
? |
139 |
℃ |
| @264 psi (1.8Mpa),
unanneled |
|
258 |
? |
126 |
℃ |
| Vicat Softening
Point, 50℃/hr, 50N Load |
ASTM D1525 |
297 |
? |
147 |
℃ |
| Coefficient of
Linear Thermal Expansion, @-40 to 82℃ |
ASTM D696 |
38ⅹ10-6 |
in/in/? |
68ⅹ10-6 |
mm/mm/℃ |
| Mechanical |
| Tensile Yield Strength3 |
ASTM D638 |
8,700 |
psi |
60 |
MPa |
| Ultimate Tensile
Strength |
ASTM D638 |
9,500 |
psi |
66 |
MPa |
| Elongation at
Yield |
ASTM D638 |
6 |
% |
6 |
% |
| Elongation at Break |
ASTM D638 |
120 |
% |
120 |
% |
| Tensile Modulus |
ASTM D638 |
340,000 |
psi |
2,340 |
MPa |
| Flexural Strength |
ASTM D790 |
14,000 |
psi |
96 |
MPa |
| Flexural Modulus |
ASTM D790 |
350,000 |
psi |
2,410 |
MPa |
| Notched Izod Impact4
@23℃ |
ASTM D256 |
14 |
ft-Ib/in |
750 |
J/m |
| unnotched Izod
Impact @23℃ |
ASTM D256 |
No break |
|
No break |
|
| Instrumented Dart
Impact5 Total Energy @23℃ |
ASTM D3763 |
640 |
in-lb |
87 |
J |
| Rockwell Hardness |
ASTM D785 |
118 |
R Scale |
72 |
M Scale |
| Taber Arasion Resistance5
(?Haze) |
ASTM D1044 |
45 |
% |
45 |
% |
| Ignition Resistance7 |
| UL-94 @1.6mm |
ASTM D635 |
HB |
|
HB |
|
| UL-94 @3.2mm |
ASTM D635 |
HB |
|
HB |
|
| Limiting Oxygen
Index |
ASTM D2863 |
26 |
% |
26 |
% |
| Ball Indentation
Temperature |
IEC 598-1 |
>125 |
℃ |
>125 |
℃ |
| Averae Extent
of Burning |
ASTM D635 |
1 |
in |
25 |
mm |
| Electrical |
| GWT 2.0mm, 5 second |
IEC 695-2-1 |
850 |
℃ |
850 |
℃ |
| Compression Tracking
Index @ 2.0mm |
IEC 112 |
250 |
V |
250 |
V |
| Dielectric Strength |
ASTM D149 |
420 |
V/mil |
17 |
KV/mm |
| Dielectric Constant
@ 60Hz |
ASTM D150 |
3 |
|
3 |
|
| Dissipation Factor
@ 60Hz |
ASTM D150 |
0.001 |
|
0.001 |
|
| Volume Resistivity
@ 23℃, dry |
ASTM D257 |
2.0x1017 |
?-cm |
2.0x1017 |
?-cm |
|
|
|
|
|
|
|
| 分 類 |
グレード |
| 物 性 |
単 位 |
ASTM |
テスト条件 |
LEXAN 121 |
| 比重 |
|
D
792 |
|
1.20 |
| 吸収率 |
% |
D
570 |
23℃, 24時間 |
0.15 |
| 成型収縮率 |
X 10 mm/mm |
D
955 |
|
5 ~ 7 |
| HDT |
℃ |
D
648 |
4.6kg/? |
138 |
|
|
|
18.6kg/? |
132 |
| 熱変形温度 |
X 10 mm/mm℃ |
D
696 |
-30℃ ~ +30℃ |
7 |
| 難燃度 |
|
UL
94 |
1.6mm 厚さ |
V - 0 |
| 厚さ |
kg/? |
D
638 |
23℃ |
630 |
| 延伸? |
% |
D
638 |
23℃ |
90 |
| 曲げ強度 |
kg/? |
D
790 |
23℃ |
920 |
| 曲げ弾性率 |
X 10 kg/? |
D
790 |
23℃ |
23 |
| Izod衝撃強度 |
kg ・ cm/cm |
D
256 |
23℃, nochitype
3.2mmthickness |
65 |
| Rockwell硬度 |
|
D
785 |
R scale |
118 |
| 誘電率 |
|
D
150 |
60Hz |
3.0 |
|
|
|
10 Hz |
3.0 |
| Power
factor |
|
D
150 |
60Hz |
0.0009 |
|
|
|
10Hz |
0.01 |
| 表面抵抗 |
Ω |
D
257 |
23℃ |
|
| 体積抵抗 |
Ω ・ cm |
D
257 |
23℃ |
10 |
|
|
 |
|
 |
| |
|
|
| Division |
Unit |
LUPOX TE-5016F |
| CylinderTemperature |
Rear |
℃ |
240~260 |
| Center |
℃ |
250~270 |
| Front |
℃ |
250~270 |
| Nozzle
Temperature |
℃ |
260~280 |
| Melt
Temperature |
℃ |
260~280 |
| Mold
Temperature |
℃ |
40~80 |
| InjectionPressure |
First |
kg/cm2 |
500~800 |
| |
Second |
kg/cm2 |
450~650 |
| |
Back |
kg/cm2 |
0~40 |
| Screw
Speed |
rpm |
70~100 |
| Typical Properties |
Unit |
Standard |
LUPOX TE-5016F |
| Specific
Gravity |
- |
ASTM D792 |
1.27 |
| Mold
Shrinkage |
cm/cm x 10-3 |
LG Chem. |
7~10 |
| Tensile
Strength |
kg/cm2 |
ASTM D 638 |
600 |
| Elongation,
break |
% |
ASTM D 638 |
60 |
| Flexural
Strength |
kg/cm2 |
ASTM D 790 |
900 |
| Flexural
Modulus |
kg/cm2 |
ASTM D 790 |
24,500 |
| IzodNotch |
23℃ |
kg.cm/cm |
ASTM D 256 |
73.5 |
| -30℃ |
|
|
22 |
| HDT
(18.6kg/cm2) |
℃ |
ASTM D 648 |
98 |
| MI
(250℃, 5kg) |
g/10min |
ASTM D 1238 |
30 |
| Flammability |
|
UL 94 |
V-0(1/8”) |
|
|
|
|
|
|
|